| GB1220-92GB3280-92 | AISIUNS | BS970BS1449 | DIN17440DIN17224 | NFA35-575NFA35-576 | ГОСТ5632 | |
| 0Cr13 | SUS410S | S410 | ||||
| 1Cr13 | SUS410 | 410 | 410S21 | X7Cr13 | Z6C13 | 08X13 |
| 2Cr13 | SUS420J1 | 420J1 | 420S29 | X20Cr13 | Z20C13 | 20x13 |
| 1Cr17 | SUS430 | 430 | ||||
| 7Cr17 | SUS440A | 440A | ||||
| 9Cr18 | SUS440C | 440C | X105CrMo17 | Z100CD17 | 95X18 | |
| 0Cr18Ni9 | SUS304 | 304 | 304S15 | X5CrNi189 | Z6CN18.09 | 08X18H10 |
| 00Cr19Ni10 | SUS304L | 304L | 304S12 | X2CrNi189 | Z2CN18.09 | 03X18H11 |
| 0Cr17Ni12Mo2 | SUS316 | 316 | 316S16 | X5CrNiMo1812 | Z6CND17.12 | |
| 00Cr17Ni14Mo2 | SUS316L | 316L | 316S12 | X2CrNiMo1812 | Z2CND17.12 | 03X17H14M2 |
| 0Cr18Ni11Ti | SUS321 | 321 | X10CrNiTi189 | Z6CNT18.10 | 08X18H10T | |
| 0Cr18Ni11Nb | SUS347 | 347 | 347S17 | X10CrNiNb189 | Z6CNNb18.10 | 08X18H12F |
表2马氏体、铁素体、奥氏体、双相不锈钢的化学成分
| 类 型 |
钢 号 | 牌 号 | |||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | 其它 | |||
| 奥 氏 体 型 |
201 | 1Cr17Mn6Ni5N | ≤0.15 | 16.00-18.00 | 3.50-5.50 | 5.50－7.50 | ≤0.060 | ≤0.030 | - | ≤1.00 | - | ≤0.25 | - |
| 201L | 03Cr17Mn6Ni5N | ≤0.030 | 16.00-18.00 | 3.50-5.50 | 5.50－7.50 | ≤0.060 | ≤0.030 | ≤1.00 | ≤0.25 | ||||
| 202 | 1Cr18Mn8Ni5N | ≤0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0.060 | ≤0.030 | ≤1.00 | - | ≤0.25 | － | ||
| 204 | 03Cr16Mn8Ni2N | ≤0.030 | 15.00-17.00 | 1.50-3.50 | 7.00-9.00 | 0.15-0.30 | |||||||
| 国内研制 | 1Cr18Mn10Ni5Mo3N | ≤0.10 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | 2.80-3.50 | 0.20-0.30 | ||||||
| 前苏联 | 2Cr13Mn9Ni4 | 0.15-0.25 | 12.00-14.00 | 3.70-5.00 | 8.00-10.00 | ||||||||
| 国内研制 | 2Cr15Mn15Ni2N | 0.15-0.25 | 14.00-16.00 | 1.50-3.00 | 14.00-16.00 | 0.15-0.30 | |||||||
| 1Cr18Mn10Ni5Mo3N | ≤0.15 | 17.00-19.00 | 4.00-6.00 | 8.50-12.00 | ≤0.060 | ≤0.030 | 2.8-3.5 | ≤1.00 | - | 0.20-0.30 | - | ||
| 301 | 1Cr17Ni7 | ≤0.15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0.065 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 302 | 1Cr18Ni9 | ≤0.15 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 303 | Y1Cr18Ni9 | ≤0.15 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0.20 | ≤0.030 | 1) | ≤1.00 | - | - | - | |
| 303se | Y1Cr18Ni9Se | ≤0.15 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0.20 | ≤0.030 | - | ≤1.00 | - | - | Se≥0.15 | |
| 304 | 0Cr18Ni9 | ≤0.07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304L | 00Cr19Ni10 | ≤0.030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304N1 | 0Cr19Ni9N | ≤0.08 | 18.00-20.00 | 7.00-10.50 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | 0.10-0.25 | - | |
| 304N2 | 0Cr18Ni10NbN | ≤0.08 | 18.00-20.00 | 7.50-10.50 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | 0.15-0.30 | Nb≤0.15 | |
| 304LN | 00Cr18Ni10N | ≤0.030 | 17.00-19.00 | 8.50-11.50 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | 0.12-0.22 | - | |
| 305 | 1Cr18Ni12 | ≤0.12 | 17.00-19.00 | 10.50-13.00 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309S | 0Cr23Ni13 | ≤0.08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 310S | 0Cr25Ni20 | ≤0.08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 316 | 0Cr17Ni12Mo2 | ≤0.08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 1Cr18Ni12Mo2Ti6) | ≤0.12 | 16.00-19.00 | 11.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 1.80-2.50 | ≤1.00 | - | - | Ti5(C%-0.02)~0.08 | ||
| 0Cr18Ni12Mo2Ti | ≤0.08 | 16.00-19.00 | 11.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 1.80-2.50 | ≤1.00 | - | - | Ti5*C%-0.70 | ||
| 316L | 00Cr17Ni14Mo2 | ≤0.030 | 16.00-18.00 | 12.00-15.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316N | 0Cr17Ni12Mo2N | ≤0.08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | 0.10-0.22 | - | |
| 316N | 00Cr17Ni13Mo2N | ≤0.030 | 16.00-18.50 | 10.50-14.50 | ≤2.00 | ≤0.035 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | 0.12-0.22 | - | |
| 316J1 | 0Cr18Ni12Mo2Cu2 | ≤0.08 | 17.00-19.00 | 10.00-14.50 | ≤2.00 | ≤0.035 | ≤0.030 | 1.20-2.75 | ≤1.00 | 1.00-2.50 | - | - | |
| 316J1L | 00Cr18Ni14Mo2Cu2 | ≤0.030 | 17.00-19.00 | 12.00-16.00 | ≤2.00 | ≤0.035 | ≤0.030 | 1.20-2.75 | ≤1.00 | 1.00-2.50 | - | - | |
| 317 | 0Cr19Ni13Mo3 | ≤0.12 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.035 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | - | - | |
| 317L | 00Cr19Ni13Mo3 | ≤0.08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.035 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | - | - | |
| 1Cr18Ni12Mo3Ti6) | ≤0.12 | 16.00-19.00 | 11.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.50-3.50 | ≤1.00 | - | - | Ti5(C%-0.02)~0.08 | ||
| 0Cr18Ni12Mo3Ti | ≤0.08 | 16.00-19.00 | 11.00-14.00 | ≤2.00 | ≤0.035 | ≤0.030 | 2.50-3.50 | ≤1.00 | - | - | Ti5*C%-0.70 | ||
| 317J1 | 0Cr18Ni16Mo5 | ≤0.040 | 16.00-19.00 | 15.00-17.00 | ≤2.00 | ≤0.035 | ≤0.030 | 4.00-6.00 | ≤1.00 | - | - | - | |
| 321 | 1Cr18Ni9Ti6) | ≤0.12 | 17.00-19.00 | 8.00-11.00 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C%-0.02)~0.08 | |
| 0Cr18Ni10Ti | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | Ti≥5*C% | ||
| 347 | 0Cr18Ni11Nb | ≤0.08 | 17.00-19.00 | 9.00-13.00 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | Nb≥10*C% | |
| XM7 | 0Cr18Ni9Cu3 | ≤0.08 | 17.00-19.00 | 8.50-10.50 | ≤2.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | 3.00-4.00 | - | - | |
| XM15J1 | 0Cr18Ni13Si4 | ≤0.08 | 15.00-20.00 | 11.50-15.00 | ≤2.00 | ≤0.035 | ≤0.030 | - | 3.00-5.00 | - | - | 2) | |
| 奥氏体 | 铁素体 |
329J1 | 0Cr26Ni5Mo2 | ≤0.08 | 23.00-28.00 | 3.00-6.00 | ≤1.50 | ≤0.035 | ≤0.030 | 1.00-3.00 | ≤1.00 | - | - | 2) |
| 1Cr18Ni11Si4AlTi | 0.10-0.18 | 17.50-19.50 | 10.--120.. | ≤0.80 | ≤0.035 | ≤0.030 | - | 3.40-4.00 | - | - | Al 0.10-0.30; Ti 0.40-0.70 | ||
| 00Cr18Ni5MoSi2 | ≤0.030 | 18.00-19.50 | 4.50-5.50 | 1.00-2.00 | ≤0.035 | ≤0.030 | 2.50-3.00 | 1.30-2.00 | - | - | - | ||
| 铁 素 体 型 |
405 | 0Cr13Al | ≤0.08 | 11.50-14.50 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | Al 0.10-0.30 |
| 410L | 00Cr12 | ≤0.030 | 11.00-13.00 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 430 | 1Cr17 | ≤0.12 | 16.00-18.00 | 3) | ≤1.25 | ≤0.035 | ≤0.030 | - | ≤0.75 | - | - | - | |
| 430F | Y1Cr17 | ≤0.12 | 16.00-18.00 | 3) | ≤1.00 | ≤0.035 | ≥0.15 | 1) | ≤1.00 | - | - | - | |
| 434 | 1Cr17Mo | ≤0.12 | 16.00-18.00 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | 0.75-1.25 | ≤1.00 | - | - | - | |
| 447J1 | 00Cr30Mo2 | ≤0.010 | 28.50-32.00 | - | ≤0.40 | ≤0.035 | ≤0.030 | 1.50-2.50 | ≤0.40 | - | ≤0.015 | - | |
| XM27 | 00Cr27Mo | ≤0.010 | 25.00-27.50 | - | ≤0.40 | ≤0.035 | ≤0.030 | 0.75-1.50 | ≤0.40 | - | ≤0.015 | - | |
| 马 氏 体 型 |
403 | 1Cr12 | ≤0.15 | 11.50-13.00 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤0.50 | - | - | - |
| 410 | 1Cr13 | ≤0.15 | 11.50-13.50 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 405 | 0Cr13 | ≤0.08 | 11.50-13.50 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 416 | Y1Cr13 | ≤0.15 | 12.00-14.00 | 3) | ≤1.25 | ≤0.035 | ≥0.15 | 1) | ≤1.00 | - | - | - | |
| 410J1 | 1Cr13Mo | ≤0.08-0.18 | 11.50-14.00 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | 0.30-0.60 | ≤0.60 | - | - | - | |
| 420J1 | 2Cr13 | 0.16-0.25 | 12.00-14.00 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0.26-0.35 | 12.00-14.00 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 420F | Y3Cr13 | 0.26-0.40 | 12.00-14.00 | 3) | ≤1.25 | ≤0.035 | ≥0.15 | 1) | ≤1.00 | - | - | - | |
| 3Cr13Mo | 0.28-0.35 | 12.00-14.00 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | 0.50-1.00 | ≤0.80 | - | - | - | ||
| 4Cr13 | 0.36-0.45 | 12.00-14.00 | 3) | ≤0.80 | ≤0.035 | ≤0.030 | - | ≤0.60 | - | - | - | ||
| 431 | 1Cr17Ni2 | 0.11-0.17 | 16.00-18.00 | 1.50-2.50 | ≤0.80 | ≤0.035 | ≤0.030 | - | ≤0.80 | - | - | - | |
| 440A | 7Cr17 | 0.60-0.75 | 16.00-18.00 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | 4) | ≤1.00 | - | - | - | |
| 440B | 8Cr17 | 0.75-0.95 | 16.00-18.00 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | 4) | ≤1.00 | - | - | - | |
| 9Cr18 | 0.90-1.00 | 17.00-19.00 | 3) | ≤0.80 | ≤0.035 | ≤0.030 | 4) | ≤0.80 | - | - | - | ||
| 440C | 11Cr17 | 0.95-1.20 | 16.00-18.00 | 3) | ≤1.00 | ≤0.035 | ≤0.030 | 4) | ≤1.00 | - | - | - | |
| 440F | Y11Cr17 | 0.95-1.20 | 16.00-18.00 | 3) | ≤1.25 | ≤0.035 | ≥0.15 | 4) | ≤1.00 | - | - | - | |
| 9Cr18Mo | 0.95-1.10 | 16.00-18.00 | 3) | ≤0.80 | ≤0.035 | ≤0.030 | 0.40-0.70 | ≤0.80 | - | - | - | ||
| 9Cr18MoV | 0.85-0.95 | 17.00-19.00 | 3) | ≤0.80 | ≤0.035 | ≤0.030 | 1.00-1.30 | ≤0.80 | - | - | V0.07-0.12 | ||
| 沉 淀 硬 化 型 |
630 | 0Cr17Ni4Cu4Nb | ≤0.07 | 15.50-17.50 | 6.50-7.50 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0.15-0.45 |
| 631 | 0Cr17Ni7Al | ≤0.09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | ≤0.50 | - | Al 0.75-1.50 | |
| 632 | 0Cr15Ni7Mo2Al | ≤0.09 | 14.00-16.00 | 6.50-7.50 | ≤1.00 | ≤0.035 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | Al 0.75-1.50 | |