| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | --- | ASTM D-1238 | 7.0 | g/10min. |
| 机械性能 | 弯曲强度 | --- | ASTM D-790 | 800(78) | kg/cm2(MPa) |
| 抗张强度 | --- | ASTM D-638 | 420(41) | kg/cm2(MPa) | |
| 抗张模数 | --- | ASTM D-638 | 1.8(1770) | kg/cm20000(MPa) | |
| 伸长率 | --- | ASTM D-638 | 2.1 | % | |
| 弯曲模数 | --- | ASTM D-790 | 3.4(3330) | kg/cm20000(MPa) | |
| Izod冲击强度 | --- | ASTM D-256 | 1.8(18) | kg-cm/cm(J/m) | |
| 热 性 能 | 卫氏软化点 | --- | ASTM D-1525 | 93 | ℃ |
| 卫氏软化点 | --- | ASTM D-648 | 93 | ℃ | |
| 热变形温度 | --- | ASTM D-1525 | 88 | ℃ | |
| 热变形温度 | --- | ASTM D-648 | 88 | ℃ | |
| 其它性能 | 残留单体 | --- | --- | 700 | ppm max |
| 燃烧性 | 1/16" | --- | HBNC | ||