| 【中文篇名】 | K6C、K18铸造高温合金焊接热裂纹敏感性的研究 |
| 【英文篇名】 | STUDY ON WELD HOT CRACKING SENSITIVITY IN CAST SUPERALLOYS K6C AND K18 |
| 【作者】 | 史常瑾; 钟祖桂; 沙允慈; 曹杨初; |
| 【英文作者】 | Shi Changjin; Zhong Ztigui; Sha Yunci and Cao Yangchu; |
| 【文献出处】 | 航空材料 , [英文刊名], 编辑部邮箱 1981年 S2期 期刊荣誉：中文核心期刊要目总览 ASPT来源刊 CJFD收录刊 |
| 【中文关键词】 | 铸造镍基高温合金; 焊接热裂纹; 焊接线能量; 色相; 热裂纹敏感性; 焊丝; 填丝; 铸造高温合金; 液体膜; |
| 【摘要】 | 本文通过刚性平板直焊缝及环形焊缝两种焊接裂纹倾向试验方法,着重研究了焊接线能量和不同填充焊丝对K6C、K18铸造镍基高温合金焊接热裂纹的影响,并测试了热裂纹敏感的温度范围,对两种合金焊接裂纹形成原因进行了金相分析,提出了改善焊接热裂纹敏感性的措施。 |
| 【英文摘要】 | In this paper, two methods for weld cracking tendency determination, namely, bead-on-plate and weld-circle tests on the restrained plates were used to study the effect of welding heat input and different kinds of filler wires on weld hot cracking in cast Ni-base superalloys K6C and Kl8. The temperature ranges which are sensitive to hot cracking were also measured. The causes of weld cracking formation in the two alloys was revealed by metallo-graphic analysis. Finally, some effective measures to improve wel… |
| 【DOI】 | CNKI:SUN:CLGC.0.1981-S2-003 |
| 【正文快照】 | 一、前 .J一 巨 随着航空工业的发展,铸造高温合金的焊接结构件日益增多。例如:导向叶片锁板组合焊接; 精铸导向叶片与内、外环的焊接:叶片堆焊耐磨层; 空心叶片堵头及精铸叶片、整铸件的修补等都对铸造高温合金的焊接技术提出了更为迫切的要求。 由于使用性能的要求,这类合金中 |