| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 其它性能 | Izod冲击强度（缺口） | 6.4mm | ASTM D-256 | 6.5 | kg？cm/cm |
| 物理性能 | 洛氏硬度 | --- | ASTM D-785 | 115 | R |
| 密度 | --- | ASTM D-792 | 1.15 | g/cm3 | |
| 机械性能 | Izod冲击强度（缺口） | 3.2mm | ASTM D-256 | 6.5 | kg？cm/cm |
| 拉伸强度 | --- | ASTM D-638 | 800 | kg/cm2 | |
| 拉伸断裂伸长率 | --- | ASTM D-638 | 10 | kg/cm2 | |
| 弯曲强度 | --- | ASTM D-790 | 900 | kg/cm2 | |
| 弯曲弹性模量 | --- | ASTM D-790 | 40000 | kg/cm2 | |
| 电气性能 | 介电强度 | --- | ASTM D-149 | 27 | KV/mm |
| 体积电阻率 | --- | ASTM D-257 | 1016 | Ωcm | |
| 加工性能 | 成型收缩率 | --- | ASTM D-955 | 0.2 | % |
| 热 性 能 | 熔融指数 | 230℃×21.6kg | ASTM D-1238 | 100 | g/10min |
| 热变形温度 | --- | ASTM D-648 | 110 | ℃ | |