镀铝膜复合气泡袋
2010-01-03 15:07:50 阅读1 评论0 字号：大中小
具有两层结构，有体积轻又环保的优点。外层为镀铝膜，内衬气泡膜。袋子美观大方，其独特的韧性可防止袋子破裂；内层透明气泡具备良好的缓冲减震作用，防止所装物品因压，碰，跌落、、、而损坏。适用于邮寄光盘碟片，磁带，电子元件，集成电路板，光学镜头，书籍，证件，相框，礼品，钟表等物品，是个人寄件，公司寄样的{sx}用品。
技术参数
| 项目 | 单位 | 检验标准 | 检验结果 |
| 密度（VMPET）/（LDPE） | g/cm |
| 1.40-0.92 |
| 拉伸强度纵向 VMPET/LDPE | Mpa | GB/96-04-10 | 200/50 |
| 拉伸强度横向VMPET/LDPE | Mpa | GB/96-04-10 | 230/25 |
| 伸长率纵向 VMPET/LDPE | % | GB/96-04-10 | 100/380 |
| 伸长率横向 VMPET/LDPE | % | GB/96-04-10 | 95/650 |
| 撕裂强度VMPET | N/25UM | GB/T-11999 | 140 |
| 撕裂强度VMPE纵向/横向 | N/25UM | GB/T-11999 | 1000/90 |
| 动磨擦系数VMPET/LDPE |
| GB/96-04-10 | 0.5/0.25 |
| 透湿度VMPET | RH | (G/㎡,24H)40°C90%RH) | 46 |
| 透湿度LPET | RH | (G/㎡,24H)40°C90%RH) | 10 |
| 透氧度VMPET | N/C㎡ | N/Cm 24/1.0MPG120C90% | 120 |
| 透氧度LDPE | N/C㎡ | N/C㎡ 4/1.0MPG120C90% | 4000 |
| 热封温度 | F | 170±10 | 250-375 |
| 热封时间 | 秒 | 0.3-0.5 | 0.5-3.5 |
| 热封压力 | P.S.I | 40-60 | 30-70 |
| 尺寸 | mm | GB/96-04-10 | 信封口±5;长±5mm;宽±5mm |
| 外观 |
| GB/96-04-10 | 无脱层,爆边,皱纹,翘曲,破裂,异物附着,封合边以外气泡￠≤3mm |
Bubble eushionde aluminized foil mailer
This product is made of metalized film with bubble linings,which is strong enough to prevent breach of the bag.The innerair bubbles have good cushioning effect to prevent damage of the loaded article due to pressure,collision or falling.Being the first choice for personal post and corporate sample post,it has below characteristics:
1) Superior cushioning and surface protection.
2) Many colors/designs available
3) Self-adhesive tape available.
4) Customized designs/shapes are welcomed.
5) Clean,easy and safe to use.
6) Lightweight and small volume for postage savings.
7) Multi-functions for mailing and package.
8) Can be reused.
9) Can be {bfb} recycle,and accord with the request of environmentalism.
Application:it can be used to post tape,CD,camera lens,film,certificate,IC card,mini-type machine accessory and so on goods that need protecting.
Technical parameters
| Item | Unit | Test standard | Test result |
| Density（VMPET）/（LDPE） | g/cm |
| 1.40-0.92 |
| Tensile strength:TD VMPET/LDPE | Mpa | GB/96-04-10 | 200/50 |
| Tensile strength : MD VMPET/LDPE | Mpa | GB/96-04-10 | 230/25 |
| Elongation rate:TD VMPET/LDPE | % | GB/96-04-10 | 100/380 |
| Elongation rate:MD VMPET/LDPE | % | GB/96-04-10 | 95/650 |
| Tearing strength VMPET | N/25UM | GB/T-11999 | 140 |
| Tearing strength LDPE TD/MD | N/25UM | GB/T-11999 | 1000/90 |
| Dynamicfriction coefficient:VMPET/LDPE |
| GB/96-04-10 | 0.5/0.25 |
| Moisture transmission VMPET | RH | (G/㎡,24H)40°C90%RH) | 46 |
| Moisture transmission LDPE | RH | (G/㎡,24H)40°C90%RH) | 10 |
| Oxygen transmission VMPET | N/C㎡ | N/Cm 24/1.0MPG120C90% | 120 |
| Oxygen transmission LDPE | N/C㎡ | N/C㎡ 4/1.0MPG120C90% | 4000 |
| Heat seal temperature | F | 170±10 | 250-375 |
| Heat seal time | Sec. | 0.3-0.5 | 0.5-3.5 |
| Heatseal pressure | P.S.I | 40-60 | 30-70 |
| Size | mm | GB/96-04-10 | Flap±5mm;Length±5mm;Width±5mm |
| Appearance |
| GB/96-04-10 | No delamination,burst seal,wrinkle,warp,break,foreign particle adherence,air bubble beyond sealing￠≤3mm |