| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔融指数 | 230°C,3.8kg | ASTM D-1238 | 15 | g/10min |
| 成型收缩率 | --- | ASTM D-955 | 0.2-0.6 | % | |
| 比重 | --- | ASTM D-792 | 1.07 | --- | |
| 吸水率 | --- | ASTM D-570 | 0.03 | % | |
| 机械性能 | 抗拉强度 | 23°C | ASTM D-638 | 800 | kg/cm2(psi) |
| 伸长率 | --- | ASTM D-638 | 4.0 | % | |
| 弯曲强度 | 23°C | ASTM D-790 | 1100 | kg/cm2(psi) | |
| 弯曲模量 | 23°C | ASTM D-790 | 36000(511200) | kg/cm2(psi) | |
| IZPD冲击强度 | 3.2mm,Notched(1/8in) | ASTM D-256 | 2.0 | kg.cm/cm(ft.ld/in) | |
| 洛氏硬度 | --- | ASTM D-785 | 88 | M scale | |
| 电气性能 | 体积电阻率 | --- | ASTM D-257 | 1016↑ | Ωcm |
| 诱电率 | --- | ASTM D-150 | 2.5↓ | 106cyl/s | |
| 耐电压 | --- | ASTM D-149 | 550↑ | v/mil | |
| 热 性 能 | 微卡软化点 | --- | ASTM D-1525 | 108(212) | °C（°F） |
| 热变形温度 | 6.4mm,18.6kg/cm2Unannealed | ASTM D-648 | 94(201) | °C（°F） | |
| 热变形温度 | 6.4mm,18.6kg/cm2Annealed | ASTM D-648 | 100(212) | °C（°F） | |
| 防燃度 | UL 94* | HB | HB | CLASS | |
| 其它性能 | 食品卫生性 | FDA | 合否 | 适合 | --- |