性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 熔体流动速率 | 200℃/5kg | ASTM D-1238 | 4.2 | g/10min |
物理性能 | 比重 | ASTM D-792 | 1.04 | g/cm3 | |
模具收缩率 | Flow | ASTM D-955 | 0.40-0.70 | % | |
机械性能 | 拉伸屈服强度 | ASTM D-638 | 53.8 | MPa | |
拉伸屈服伸长率 | ASTM D-638 | 20 | % | ||
弯曲模量 | ASTM D-790 | 2550 | MPa | ||
弯曲屈服强度 | ASTM D-790 | 71.7 | MPa | ||
IZOD缺口冲击强度 | 23℃,3.18mm | ASTM D-256 | 176 | J/m | |
IZOD缺口冲击强度 | 23℃,6.35mm | ASTM D-256 | 139 | J/m | |
洛氏硬度 | ASTM D-785 | 115 | R scale | ||
电气性能 | 体积电阻率 | ASTM D-257 | 1.0E+12 | ohm.cm | |
热性能 | 热变形温度 | 1.80MPa,未退火 | ASTM D-648 | 87.2 | ℃ |
维卡软化温度 | ASTM D-1525 | 97.8 | ℃ | ||
燃烧性 | 1.65mm | UL 94 | HB | ||
燃烧性 | 3.18mm | UL 94 | HB |