PMMA IH830 LG化学亚克力塑料原料
面议
|
性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
|
|
物理性能
|
比重
|
|
ASTM D792
|
1.18
|
|
|
熔流率
|
230℃/3.8Kg
|
ASTM D1238
|
2.2
|
g/10min
|
|
|
收缩率
|
流动
|
ASTM D955
|
0.20-0.60
|
%
|
|
|
吸水率
|
24hr
|
ASTM D570
|
0.30
|
%
|
|
|
洛氏硬度
|
M 计秤
|
ASTM D785
|
98
|
|
|
|
机械性能
|
抗张强度
|
屈服
|
ASTM D638
|
72.6
|
MPa
|
|
伸长率
|
屈服
|
ASTM D638
|
10
|
%
|
|
|
弯曲模量
|
|
ASTM D790
|
3360
|
MPa
|
|
|
弯曲强度
|
屈服
|
ASTM D790
|
136
|
MPa
|
|
|
悬臂梁缺口冲击强度
|
|
ASTM D256
|
15
|
J/m
|
|
|
热性能
|
热变形温度
|
1.8MPa,未退火
|
ASTM D648
|
94.0
|
℃
|
|
维卡软化温度
|
|
ASTM D1525
|
113
|
℃
|
|
|
线性膨胀系数
|
流动
|
ASTM D696
|
0.000060
|
cm/cm/℃
|
|
|
RTI Elec
|
1.50mm
|
UL 746
|
50.0
|
℃
|
|
|
RTI Imp
|
1.50mm
|
UL 746
|
50.0
|
℃
|
|
|
RTI Str
|
1.50mm
|
UL 746
|
50.0
|
℃
|
|
|
可燃性
|
UL阻燃等级
|
|
UL 94
|
HB
|
|
|
|
1.50mm,AII
|
UL 94
|
HB
|
|
|
|
光学性能
|
折射率
|
|
ASTM D542
|
1.490
|
|
|
透射率
|
3000um
|
ASTM D1003
|
92.0
|
%
|
|
|
雾度
|
3000um
|
ASTM D1003
|
0.50
|
%
|
|
|
黄度指数
|
3.00mm
|
ASTM D1925
|
0.40
|
YI
|
|