PMMA IF860 LG化学亚克力塑料原料
面议
|
性能项目
|
试验条件[状态]
|
测试方法
|
测试数据
|
数据单位
|
|
|
物理性能
|
比重
|
|
ASTM D792
|
1.18
|
g/cm3
|
|
吸水率
|
24hr
|
ASTM D570
|
0.3
|
%
|
|
|
流动指数
|
230℃,3.8kg
|
ASTM D1238
|
16
|
g/10min
|
|
|
洛氏硬度
|
M-scale
|
ASTM D785
|
94
|
|
|
|
机械性能
|
IZOD冲击强度
|
with notch
|
ASTM D256
|
1.5
|
kg·cm/cm2
|
|
拉力
|
|
ASTM D638
|
660
|
Kg/cm2
|
|
|
延伸率
|
|
ASTM D638
|
10
|
Kg/cm2
|
|
|
弯曲强度
|
|
ASTM D790
|
1.310
|
Kg/cm2
|
|
|
弯曲模量
|
|
ASTM D790
|
33600
|
Kg/cm2
|
|
|
热性能
|
维卡软化点
|
1kg
|
ASTM D1525
|
104
|
°C
|
|
热变形温度
|
未退火,18.5kg/cm2
|
ASTM D648
|
84
|
°C
|
|
|
线性膨胀系数
|
|
ASTM D696
|
6*10-5
|
cm/cm/°C
|
|
|
其它
|
折射率
|
nd
|
ASTM D542
|
1.49
|
|
|
透明性
|
3mm
|
ASTM D1003
|
92
|
%
|
|
|
黄色度
|
3mm
|
ASTM D1925
|
0.4
|
%
|
|
|
HAZE
|
3mm
|
ASTM D1003
|
0.5
|
%
|
|